Химический состав жаропрочных и нержавеющих сталей
|
|
Химический состав |
Заменители |
|||||||||||||
|
Коррозионностойкие стали |
Обозначение по DIN EN 10088 |
C, % max |
Si, % max |
Mn, % Max |
Cr, % |
Mo, % |
Ni,% |
Другие, % |
США AISI |
Япония JIS |
СНГ ГОСТ |
||||
|
ФЕРРИТНЫЕ И МАРТЕНСИТНЫЕ СТАЛИ |
|||||||||||||||
|
1.4003 |
X2CrNi12 |
0.03 |
1.00 |
1.50 |
10.50-12.50 |
|
0.30-1.00 |
N:<0.030 |
|
|
|
||||
|
1.4512 |
X2CrTi12 |
0.08 |
1.00 |
1.00 |
10.50-12.50 |
|
|
6x(C+N)<Ti<0.65 |
409 |
SUH 409 |
|
||||
|
1.4000 |
X6Cr13 |
0.08 |
1.00 |
1.00 |
12.00-14.00 |
|
|
|
410S |
SUS 410S |
08Х13 |
||||
|
1.4002 |
X6CrAl13 |
0.08 |
1.00 |
1.00 |
12.00-14.00 |
|
|
Al:0.10-0.30 |
405 |
SUS 405 |
|
||||
|
1.4006 |
X12CrNi13 |
0.08-0.15 |
1.00 |
1.50 |
11.50-13.50 |
|
<0.75 |
|
410 |
SUS 410 |
12Х13 |
||||
|
1.4024 |
X15Cr13 |
0.12-0.17 |
1.00 |
1.00 |
12.00-14.00 |
|
|
|
(410) |
SUS 410J1 |
15Х13Л |
||||
|
1.4021 |
X20Cr13 |
0.16-0.25 |
1.00 |
1.50 |
12.00-14.00 |
|
|
|
(420) |
SUS 420J1 |
20Х13 |
||||
|
1.4028 |
X30Cr13 |
0.26-0.35 |
1.00 |
1.50 |
12.00-14.00 |
|
|
|
(420) |
SUS 420J2 |
30Х13 |
||||
|
1.4031 |
X39Cr13 |
0.36-0.42 |
1.00 |
1.00 |
12.50-14.50 |
|
|
|
|
SUS 410J2 |
40Х13 |
||||
|
1.4034 |
X46Cr13 |
0.43-0.50 |
1.00 |
1.00 |
12.50-14.50 |
|
|
Ti:0.30-0.60 |
(420) |
|
40Х13 |
||||
|
1.4016 |
X6Cr17 |
0.08 |
1.00 |
1.00 |
16.00-18.00 |
|
|
N:<0.015 |
430 |
SUS 430 |
12Х17 |
||||
|
1.4520 |
X2CrTi17 |
0.025 |
0.50 |
0.50 |
16.00-18.00 |
|
|
4x(C+N) |
|
|
|
||||
|
|
|
|
|
|
|
|
|
+0.15<Ti<0.80 |
|
|
|
||||
|
1.4510 |
X3CrTi17 |
0.08 |
1.00 |
1.00 |
16.00-18.00 |
|
|
|
439 |
SUS 43 LX |
08Х17Т |
||||
|
1.4113 |
X6CrMo17-1 |
0.08 |
1.00 |
1.00 |
16.00-18.00 |
0.90-1.40 |
|
Ti:0.10-0.60 |
434 |
SUS 434 |
|
||||
|
1.4509 |
X2CrTiNb18 |
0.03 |
1.00 |
1.00 |
17.50-18.50 |
1.80-2.50 |
|
4x(C+N) |
441 |
|
|
||||
|
1.4521 |
X2CrMoTi18-2 |
0.025 |
1.00 |
1.00 |
17.00-20.00 |
|
|
+0.15<Ti<0.80 |
444 |
SUS 444 |
|
||||
|
|
|
|
|
|
|
|
|
N:<0.030 |
|
|
|
||||
|
1.4589 |
X5CrNiMoTi15-2 |
0.08 |
1.00 |
1.00 |
13.50-15.00 |
0.20-1.20 |
1.00-2.50 |
Ti:0.30-0.50 |
|
|
|
||||
|
АУСТЕНИТНЫЕ СТАЛИ |
|||||||||||||||
|
1.4310 |
X10CrNi18-8 |
0.05-0.15 |
2.00 |
2.00 |
16.00-19.00 |
<0.80 |
6.00-9.50 |
|
(301) |
SUS 301 |
12Х18Н9 |
||||
|
1.4318 |
X2CrNiN18-7 |
0.03 |
1.00 |
2.00 |
16.50-18.50 |
|
6.00-8.00 |
N: 0.10-0.20 |
301LN |
SUS301LN |
|
||||
|
1.4301 |
X5CrNi18-10 |
0.07 |
1.00 |
2.00 |
17.00-19.50 |
|
8.00-10.50 |
N: <0.11 |
304 |
SUS 304 |
08Х18Н9 |
||||
|
1.4303 |
X4CrNi18-12 |
0.06 |
1.00 |
2.00 |
17.00-19.00 |
|
11.00-13.00 |
N: <0.11 |
(305) |
SUS 305 |
06Х18Н11 |
||||
|
1.4306 |
X2CrNi19-11 |
0.03 |
1.00 |
2.00 |
18.00-20.00 |
|
10.00-12.00 |
N: <0.11 |
304L |
SUS 304 L |
03Х18Н11 |
||||
|
1.4541 |
X6CrNiTi18-10 |
0.08 |
1.00 |
2.00 |
17.00-19.00 |
|
9.00-12.00 |
5xC<Ti<0.70 |
321 |
SUS 321 |
08Х18Н10Т |
||||
|
1.4550 |
X6CrNiNb18-10 |
0.08 |
1.00 |
2.00 |
17.00-19.00 |
|
9.00-12.00 |
10xC<Nb<1.00 |
347 |
SUS 347 |
08Х18Н12Б |
||||
|
1.4401 |
X5CrNiMo17-12-2 |
0.07 |
1.00 |
2.00 |
16.50-18.50 |
2.00-2.50 |
10.00-13.00 |
|
316 |
SUS 316 |
|
||||
|
1.4404 |
X2CrNiMo17-12-2 |
0.03 |
1.00 |
2.00 |
16.50-18.50 |
2.00-2.00 |
10.00-13.00 |
N: <0.11 |
316L |
SUS 316 L |
03Х17Н14М2 |
||||
|
1.4571 |
X6CrNiMoTi17-12-2 |
0.08 |
1.00 |
2.00 |
16.50-18.50 |
2.00-2.00 |
10.50-13.50 |
5xC<Ti<0.70 |
316Ti |
SUS 316 |
10Х17Н13М2Т |
||||
|
1.4561 |
X1CrNiMoTi18-13-2 |
0.02 |
0.50 |
2.00 |
17.00-18.50 |
2.00-2.50 |
11.50-13.50 |
Ti: 0.40-0.60 |
|
|
|
||||
|
1.4435 |
X2CrNiMo18-14-3 |
0.03 |
1.00 |
2.00 |
17.00-19.00 |
2.50-3.00 |
12.50-15.00 |
N: <0.11 |
316L |
SUS 316 L |
03Х17Н14М2 |
||||
|
1.4439 |
X2CrNiMoN17-13-5 |
0.03 |
1.00 |
2.00 |
16.50-18.50 |
4.00-5.00 |
12.50-14.50 |
N: <0.12-0.22 |
S31726 |
SUS 317 |
|
||||
|
1.4539 |
X1NiCrMoCu25-20-5 |
0.02 |
0.70 |
2.00 |
19.00-21.00 |
4.00-5.00 |
24.00-26.00 |
N: <0.15 Cu: 1.20-2.00 |
N08904 |
|
06ХН28МДТ |
||||
|
1.4565 |
X3CrNiMnMoNbN 23-17-5-3 |
0.04 |
1.00 |
4.5-6.5 |
21.00-25.00 |
3.00-4.50 |
15.00-18.00 |
Nb: <0.30 N: 0.30-0.50 |
S34565 |
|
|
||||
|
ФЕРРИТНО-АУСТЕНИТНЫЕ СТАЛИ |
|||||||||||||||
|
1.4462 |
X2CrNiMoN22-5-3 |
0.03 |
1.00 |
2.00 |
21.00-23.00 |
2.50-3.50 |
4.50-6.50 |
N: 0.10-0.22 |
S31803 |
SUS329J3L |
08Х22Н6Т |
||||
|
Жаропрочные и жаростойкие стали |
|
|
C,% |
Si,% |
Al,% |
Cr,% |
Ni,% |
|
Другие, % |
|
|
|
|||
|
ФЕРРИТНЫЕ СТАЛИ |
|||||||||||||||
|
1.4713 |
X10CrAl7 |
<0.12 |
0.5-1.0 |
0.5-1.0 |
6.0-8.0 |
|
|
|
|
|
15Х6СЮ |
||||
|
1.4724 |
X10CrAl13 |
<0.12 |
0.7-1.4 |
0.7-1.2 |
12.0-14.0 |
|
|
|
405 |
|
10Х13СЮ |
||||
|
1.4742 |
X10CrAl18 |
<0.12 |
0.7-1.4 |
0.7-1.2 |
17.0-19.0 |
|
|
|
442 |
|
|
||||
|
1.47.62 |
X10CrAl24 |
<0.12 |
0.7-1.4 |
1.2-1.7 |
23.0-26.0 |
|
|
|
446 |
|
|
||||
|
ФЕРРИТНЫЕ СТАЛИ |
|||||||||||||||
|
1.4878 |
X12CrNiTi18-9 |
<0.12 |
<1.0 |
|
17.0-19.0 |
9.0-11.5 |
|
4x%C<Ti<0.8 |
321H |
|
12Х18Н10Т |
||||
|
1.4828 |
X15CrNiSl20-12 |
<0.20 |
1.5-2.5 |
|
19.0-21.0 |
11.0-13.0 |
|
|
309 |
|
20Х20Н14С2 |
||||
|
1.4845 |
X12CrNi25-21 |
<0.15 |
<0.75 |
|
24.0-26.0 |
19.0-22.0 |
|
|
310S |
|
|
||||
|
1.4841 |
X15CrNiSi25-20 |
<0.20 |
1.5-2.5 |
|
24.0-26.0 |
19.0-22.0 |
|
|
314 |
|
20Х25Н20С2 |
||||